Compound and organic light emitting device including the same

ABSTRACT

A compound represented by Formula 1 below and an organic light-emitting device including the compound of Formula 1: 
                         
wherein Ar 1 , Ar 2 , Ar 3 , Ar 4 , R 1 , X, and Y in Formula 1 above are defined as in the specification.

CROSS-REFERENCE TO RELATED PATENT APPLICATION

This application claims the benefit under 35 U.S.C. §119 of Korean Patent Application No. 10-2012-0116742, filed on Oct. 19, 2012, in the Korean Intellectual Property Office, the disclosure of which is incorporated herein in its entirety by reference.

BACKGROUND

1. Field

Embodiments relate to a compound and an organic light-emitting device including the same.

2. Description of the Related Art

Organic light-emitting devices (OLEDs), which are self-emitting devices, have advantages such as wide viewing angles, excellent contrast, quick response, high brightness, excellent driving voltage characteristics, and can provide multicolored images.

A typical OLED has a structure including a substrate, and an anode, a hole transport layer (HTL), an emission layer (EML), an electron transport layer (ETL), and a cathode which are sequentially stacked on the substrate. In this regard, the HTL, the EML, and the ETL are organic thin films formed of organic compounds.

An operating principle of an OLED having the above-described structure is as follows.

When a voltage is applied between the anode and the cathode, holes injected from the anode move to the EML via the HTL, and electrons injected from the cathode move to the EML via the ETL. The holes and electrons recombine in the EML to generate excitons. When the excitons drop from an excited state to a ground state, light is emitted.

SUMMARY

Embodiments are directed to a compound represented by Formula 1 below:

wherein, in Formula 1,

R1 is a substituted or unsubstituted C1-C60 alkyl group, a substituted or unsubstituted C2-C60 alkenyl group, a substituted or unsubstituted C2-C60 alkynyl group, a substituted or unsubstituted C3-C60 cycloalkyl group, a substituted or unsubstituted C3-C60 cycloalkenyl group, a substituted or unsubstituted C5-C60 aryl group, a substituted or unsubstituted C2-C60 heteroaryl group, a substituted or unsubstituted C5-C60 aryloxy group, a substituted or unsubstituted C5-C60 arylthio group, or a substituted or unsubstituted C6-C60 condensed polycyclic group;

Ar1 to Ar4 are each independently a substituted or unsubstituted C6-C60 aryl group, a substituted or unsubstituted C2-C60 heteroaryl group, or a substituted or unsubstituted C6-C60 condensed polycyclic group; and

X and Y are each independently a single bond, a substituted or unsubstituted C6-C60 arylene group, a substituted or unsubstituted C2-C60 heteroarylene group, a substituted or unsubstituted C6-C60 condensed polycyclic group, or a divalent linking group formed by linking at least two of the substituted or unsubstituted C6-C60 arylene group, the substituted or unsubstituted C2-C60 heteroarylene group and the substituted or unsubstituted C6-C60 condensed polycyclic groups.

In Formula 1, at least two of Ar₁, Ar₂ and X may be linked to one another to form a ring, or at least two of Ar₁, Ar₄ or Y may be linked to each other to form a ring.

In Formula 1, R₁ may be a group represented by one of Formulae 2a-2g:

wherein, in Formulae 2a to 2g,

Q₀ and Q₁ are each independently a linking group represented by —C(R₃₀)(R₃₁)— or —N(R₃₂)—;

Z₁, Z₂, R₃₀, R₃₁, and R₃₂ are each independently a hydrogen atom, a deuterium atom, a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, a substituted or unsubstituted C6-C20 condensed polycyclic group, —Si(R₄₀)₃, a halogen group, a cyano group, a nitro group, a hydroxy group or carboxy group;

R₄₀ is a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, or a substituted or unsubstituted C6-C20 condensed polycyclic group;

Y₁ to Y₃ are each independently C or N;

p is an integer from 1 to 8; and

* indicates a binding site to a nitrogen atom.

In Formula 1, Ar₁ to Ar₄ may each independently be a group represented by one of Formulae 3a to 3d:

wherein, in Formulae 3a to 3d,

Q₂ is a linking group represented by —C(R₃₀)(R₃₁)—, —N(R₃₂)—, —S—, or —O—;

Z₁, R₃₀, R₃₁, and R₃₂ are each independently a hydrogen atom, a deuterium atom, a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, a substituted or unsubstituted C6-C20 condensed polycyclic group, —Si(R₄₀)₃, a halogen group, a cyano group, a nitro group, a hydroxy group, or a carboxy group;

R₄₀ is a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, or a substituted or unsubstituted C6-C20 condensed polycyclic group;

p is an integer from 1 to 7; and

* indicates a binding site to a nitrogen atom.

In Formula 1, X and Y may be each independently a group represented by one of Formulae 4a to 4g below:

wherein, in Formulae 4a to 4g,

Q₃ is a linking group represented by —C(R₃₀)(R₃₁)—, —S—, or —O—;

R₃₀ and R₃₁ are each independently a hydrogen atom, a deuterium atom, a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, a substituted or unsubstituted C6-C20 condensed polycyclic group, —Si(R₄₀)₃, a halogen group, a cyano group, a nitro group, a hydroxy group or carboxy group;

R₄₀ is a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, or a substituted or unsubstituted C6-C20 condensed polycyclic group; and

* indicates a binding site to a carbon or nitrogen atom.

The compound represented by Formula 1 may be one of the following compounds:

Embodiments are also directed to an organic light-emitting device including a first electrode, a second electrode, and an organic layer between the first electrode and the second electrode, wherein the organic layer includes the compound of claim 1.

The organic light-emitting device may include a fluorescent or phosphorescent device. The organic layer may include an emission layer in which the compound of Formula 1 is a host or dopant.

The organic layer may be a hole injection layer, a hole transport layer, or a functional layer having both hole injection and hole transport capabilities.

The organic light-emitting device may include an emission layer, an electron injection layer, an electron transport layer, a functional layer having both electron injection and transport capabilities; a hole injection layer, a hole transport layer, or a functional layer having both hole injection and transport capabilities. At least one of the hole injection layer, the hole transport layer, and the functional layer having both hole injection and hole transport capabilities further includes the compound represented by Formula 1. The emission layer may include an anthracene-based compound, an arylamine-based compound, or a styryl-based compound.

The organic light-emitting device may include an emission layer, an electron injection layer, an electron transport layer, a functional layer having both electron injection and transport capabilities, a hole injection layer, a hole transport layer, or a functional layer having both hole injection and transport capabilities. At least one of the hole injection layer, the hole transport layer, and the functional layer having both hole injection and hole transport capabilities may further include the compound represented by Formula 1. The emission layer may include red, green, blue, and white emission layers, one of which includes a phosphorescent compound.

At least one of the hole injection layer, the hole transport layer, and the functional layer having both hole injection and hole transport capabilities may further include a charge-generating material.

The charge-generating material may be a p-dopant.

The p-dopant may be a quinine derivative, a metal oxide, or a cyano group-containing compound.

The organic layer may include an electron transport layer. The electron transport layer may include a metal complex.

The metal complex may be a Li complex.

The metal complex may be lithium quinolate (LiQ).

The metal complex may be Compound 203 below:

The organic layer of the organic light-emitting device may be formed from the compound represented by Formula 1 using a wet process.

Embodiments are also directed to a flat panel display device including the organic light-emitting device, wherein the first electrode of the organic light-emitting device is electrically connected to a source electrode or a drain electrode of a thin-film transistor.

BRIEF DESCRIPTION OF THE DRAWING

Features will become apparent to those of ordinary skill in the art by describing in detail exemplary embodiments with reference to the attached drawings in which:

FIG. 1 illustrates a schematic view of a structure of an organic light-emitting device according to an embodiment.

DETAILED DESCRIPTION

As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items. Expressions such as “at least one of,” when preceding a list of elements, modify the entire list of elements and do not modify the individual elements of the list.

Embodiments may provide a compound represented by Formula 1 below.

In Formula 1,

R₁ may be a substituted or unsubstituted C1-C60 alkyl group, a substituted or unsubstituted C2-C60 alkenyl group, a substituted or unsubstituted C2-C60 alkynyl group, a substituted or unsubstituted C3-C60 cycloalkyl group, a substituted or unsubstituted C3-C60 cycloalkenyl group, a substituted or unsubstituted C5-C60 aryl group, a substituted or unsubstituted C2-C60 heteroaryl group, a substituted or unsubstituted C5-C60 aryloxy group, a substituted or unsubstituted C5-C60 arylthio group, a substituted or unsubstituted C5-C60 aryl group, or a substituted or unsubstituted C2-C60 heteroaryl group; or C6-C60 a substituted or unsubstituted condensed polycyclic group;

Ar₁ to Ar₄ may be each independently a substituted or unsubstituted C6-C60 aryl group, a substituted or unsubstituted C2-C60 heteroaryl group, or a substituted or unsubstituted C6-C60 condensed polycyclic group; and

X and Y may be each independently a single bond, a substituted or unsubstituted C6-C60 arylene group, a substituted or unsubstituted C2-C60 heteroarylene group, a substituted or unsubstituted C6-C60 condensed polycyclic group, an arylene group, heteroarylene group, or a divalent linking group formed by linking at least two of the arylene group, the heteroarylene group and the condensed polycyclic groups.

The compound of Formula 1 above may serve as a light-emitting material and/or a hole transporting material or a hole injecting material for organic light-emitting devices. The compound of Formula 1 having a condensed ring in molecules may have a high glass transition temperature (Tg) or a high melting point due to the inclusion of the condensed ring. Thus, the compound of Formula 1 may have improved heat resistance against Joule's heat generated in an organic layer, between organic layers, or between an organic layer and a metal electrode when light emission occurs, and have high durability in high-temperature environments. An organic light-emitting device manufactured using the condensed ring compound of Formula 1 may have improved durability when stored or operated.

Substituents in the compound of Formula 1 will now be described in detail.

In some embodiments, in Formula 1, Ar₁, Ar₂, or X may be linked to form a ring, and/or Ar₃, Ar₄, or Y may be linked to form a ring.

In some embodiments, in Formula 1, R₁ may be one of the groups represented by Formulae 2a to 2g.

in Formulas 2a to 2g,

Q₀ and Q₁ may be each independently a linking group represented by —C(R₃₀)(R₃₁)— or —N(R₃₂)—;

Z₁, Z₂, R₃₀, R₃₁, and R₃₂ may be each independently a hydrogen atom, a deuterium atom, a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, a substituted or unsubstituted C6-C20 condensed polycyclic group, —Si(R₄₀)₃, a halogen group, a cyano group, a nitro group, a hydroxy group, or a carboxy group;

R₄₀ may be a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, or a substituted or unsubstituted C6-C20 condensed polycyclic group;

Y₁ to Y₃ may be each independently C or N;

p is an integer from 1 to 8; and * indicates a binding site.

In some other embodiments, in Formula 1, Ar₁ to Ar₄ may be each independently one of the group represented by Formulae 3a to 3d below.

In Formula 3a to 3d,

Q₂ may be a linking group represented by —C(R₃₀)(R₃₁)—, —N(R₃₂)—, —S—, or —O—;

Z₁, R₃₀, R₃₁, and R₃₂ may be each independently a hydrogen atom, a deuterium atom, a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, a substituted or unsubstituted C6-C20 condensed polycyclic group, —Si(R₄₀)₃, a halogen group, a cyano group, a nitro group, a hydroxy group or a carboxy group;

R₄₀ may be a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, or a substituted or unsubstituted C6-C20 condensed polycyclic group;

p is an integer from 1 to 7; * indicates a binding site.

In some other embodiments, in Formula 1, X and Y may be each independently one of the groups represented by Formulae 4a to 4g below.

In Formulae 4a to 4g,

Q3 may be a linking group represented by —C(R₃₀)(R₃₁)—, —S—, or —O—;

R₃₀ and R₃₁ may be each independently a hydrogen atom, a deuterium atom, a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, a substituted or unsubstituted C6-C20 condensed polycyclic group, —Si(R₄₀)₃, a halogen group, a cyano group, a nitro group, a hydroxy group or a carboxy group;

R₄₀ may be a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, or a substituted or unsubstituted C6-C20 condensed polycyclic group; and

* indicates a binding site.

Hereinafter, substituents described with reference to the formulae will now be described in detail. In this regard, the numbers of carbons in substituents are presented only for illustrative purposes and do not limit the characteristics of the substituents.

The unsubstituted C1-C60 alkyl group may be linear or branched. Non-limiting examples of the unsubstituted C1-C60 alkyl group are methyl, ethyl, propyl, isobutyl, sec-butyl, pentyl, iso-amyl, hexyl, heptyl, octyl, nonanyl, and dodecyl. At least one hydrogen atom of the unsubstituted C1-C60 alkyl group may be substituted with a deuterium atom, a halogen atom, a hydroxy group, a nitro group, a cyano group, an amino group, an amidino group, a hydroxyrazine, a hydroxyrazone, a carboxyl group or a salt thereof, a sulfonic acid group or a salt thereof, a phosphoric acid group or a salt thereof, or a C1 to 10 alkyl group, a C1 to 10 alkoxy group, a C2 to 10 alkenyl group, a C2 to 10 alkynyl group, a C6 to 16 aryl group, a C4 to 16 heteroaryl group, or an organosilyl group.

The term “unsubstituted C2-C60 alkenyl group” indicates an unsaturated alkyl groups having at least one carbon-carbon double bond in the center or at a terminal of the alkyl group. Examples of the alkenyl group are an ethenyl group, a propenyl group, a butenyl group, and the like. At least one hydrogen atom in the unsubstituted alkenyl group may be substituted with a substituent described above in conjunction with the alkyl group.

The term “unsubstituted C2-C60 alkynyl group” indicates an alkyl group having at least one carbon-carbon triple bond in the center or at a terminal of the alkyl group. Non-limiting examples of the unsubstituted C2-C20 alkynyl group are acetylene, propylene, phenylacetylene, naphthylacetylene, isopropylacetylene, t-butylacetylene, and diphenylacetylene. At least one hydrogen atom in the alkynyl group may be substituted with a substituent described above in conjunction with the alkyl group.

The term “unsubstituted C3-C60 cycloalkyl group” indicates a C3-C60 cyclic alkyl group wherein at least one hydrogen atom in the cycloalkyl group may be substituted with a substituent described above in conduction with the C1-C60 alkyl group.

The term “unsubstituted C1-C60 alkoxy group” indicates a group having a structure of —OA wherein A is an unsubstituted C1-C60 alkyl group as described above. Non-limiting examples of the unsubstituted C1-C60 alkoxy group are a methoxy group, an ethoxy group, a propoxy group, an isopropyloxy group, a butoxy group, and a pentoxy group. At least one hydrogen atom of the alkoxy group may be substituted with a substituent such as those described above in conjunction with the alkyl group.

The term “unsubstituted C5-C60 aryl group” indicates a carbocyclic aromatic system containing at least one ring. At least two rings may be fused to each other or linked to each other by a single bond. The term ‘aryl’ refers to an aromatic system, such as phenyl, naphthyl, or anthracenyl. At least one hydrogen atom in the aryl group may be substituted with a substituent described above in conjunction with the unsubstituted C1-C60 alkyl group.

Non-limiting examples of the a substituted or unsubstituted C5-C60 aryl group include a phenyl group, a C1-C10 alkylphenyl group (for example, ethylphenyl group), a halophenyl group (for example, o-, m-, and p-fluorophenyl group, dichlorophenyl group), a cyanophenyl group, dicyanophenyl group, a trifluoromethoxyphenyl group, a biphenyl group, a halobiphenyl group, a cyanobiphenyl group, a C1-C10 alkyl biphenyl group, a C1-C10 alkoxybiphenyl group, a o-, m-, and p-tolyl group, an o-, m-, and p-cumenyl group, a mesityl group, a phenoxyphenyl group, a (α,α-dimethylbenzene)phenyl group, a (N,N-dimethyl)aminophenyl group, a (N,N′-diphenyl)aminophenyl group, a pentalenyl group, an indenyl group, a naphthyl group, a halonaphthyl group (for example, fluoronaphthyl group), a C1-C10 alkylnaphthyl group (for example, methylnaphthyl group), a C1-C10 alkoxynaphthyl group (for example, methoxynaphthyl group), a cyanonaphthyl group, an anthracenyl group, an azulenyl group, a heptalenyl group, an acenaphthylenyl group, a phenalenyl group, a fluorenyl group, an anthraquinolyl group, a methylanthryl group, a phenanthryl group, a triphenylene group, a pyrenyl group, a chrycenyl group, an ethyl-chrysenyl group, a picenyl group, a perylenyl group, a chloroperylenyl group, a pentaphenyl group, a pentacenyl group, a tetraphenylenyl group, a hexaphenyl group, a hexacenyl group, a rubicenyl group, a coronelyl group, a trinaphthylenyl group, a heptaphenyl group, a heptacenyl group, a pyranthrenyl group, and an ovalenyl group.

The unsubstituted C3-C60 heteroaryl group used herein may include one, two or three hetero atoms selected from N, O, P and S. At least two rings may be fused to each other or linked to each other by a single bond. Non-limiting examples of the unsubstituted C4-C60 heteroaryl group are a pyrazolyl group, an imidazolyl group, an oxazolyl group, a thiazolyl group, a triazolyl group, a tetrazolyl group, an oxadiazolyl group, a pyridinyl group, a pyridazinyl group, a pyrimidinyl group, a triazinyl group, a carbazole group, an indole group, a quinolyl group, an isoquinolyl group, and a dibenzothiophene group. In addition, at least one hydrogen atom in the heteroaryl group may be substituted with a substituent described above in conjunction with the unsubstituted C1-C60 alkyl group.

The unsubstituted C5-C60 aryloxy group is a group represented by —OA₁ wherein A₁ may be a C5-C60 aryl group. An example of the aryloxy group is a phenoxy group. At least one hydrogen atom in the aryloxy group may be substituted with a substituent described above in conjunction with the unsubstituted C1-C60 alkyl group.

The unsubstituted C5-C60 arylthio group is a group represented by —SA₁ wherein A₁ may be a C5-C60 aryl group. Non-limiting examples of the arylthio group are a benzenethio group and a naphthylthio group. At least one hydrogen atom in the arylthio group may be substituted with a substituent described above in conjunction with the unsubstituted C1-C60 alkyl group.

The term “unsubstituted C6-C60 condensed polycyclic group” used herein refers to a substituent including at least two rings wherein at least one aromatic ring and/or at least one non-aromatic ring are fused to each other, or refers to a substituent having an unsaturated group in a ring that may not form a conjugate structure. The unsubstituted C6-C60 condensed polycyclic group is distinct from an aryl group or a heteroaryl group in terms of being non-aromatic.

Non-limiting examples of the compound represented by Formula 1 are Compounds 1 to 68 represented by the following formulae.

Embodiments may also provide an organic light-emitting device including a first electrode, a second electrode, and an organic layer disposed between the first electrode and the second electrode, wherein the organic layer includes the compound of Formula 1 described above.

The organic layer may include at least one layer selected from among a hole injection layer, a hole transport layer, a functional layer having both hole injection and hole transport capabilities (hereinafter, “H-functional layer”), a buffer layer, an electron blocking layer, an emission layer, a hole blocking layer, an electron transport layer, an electron injection layer, and a functional layer having both electron injection and electron transport capabilities (hereinafter, “E-functional layer”).

In some embodiments, the organic layer may be an emission layer, and the compound may be used as a host in a fluorescent or phosphorescent device).

In some embodiments, the organic light-emitting device may include an electron injection layer, an electron transport layer, an emission layer, a hole injection layer, a hole transport layer, or a functional layer having both hole injection and transport capabilities; and the emission layer may include the compound of Formula 1 above, and an anthracene-based compound, an arylamine-based compound or a styryl-based compound.

In some other embodiments, the organic light-emitting device may include an electron injection layer, an electron transport layer, an emission layer, a hole injection layer, a hole transport layer, or a functional layer having both hole injection and transport capabilities; at least one of a red emission layer, a green emission layer, a blue emission layer, and a white emission layer of the emission layer may include a phosphorescent compound; and at least one of the hole injection layer, the hole transport layer, and the functional layer having both hole injection and hole transport capabilities may further include a charge-generating material, in addition to the compound of Formula 1. In some embodiments, the charge-generating material may be a p-dopant, and the p-dopant may be a quinine derivative, a metal oxide, or a cyano group-containing compound.

In some embodiments, the organic layer may include an electron transport layer, and the electron transport layer may include an electron-transporting organic compound and a metal complex. The metal complex may be a lithium (Li) complex.

The term “organic layer” as used herein refers to a single layer and/or a plurality of layers disposed between the first and second electrodes of the organic light-emitting device.

The organic layer may include an emission layer, and the emission layer may include the compound of Formula 1 described above. The organic layer may include at least one of a hole injection layer, a hole transport layer, and a functional layer having both hole injection and hole transport capabilities (hereinafter, “H-functional layer”); and at least one of the hole injection layer, the hole transport layer, and the functional layer having both hole injection and hole transport capabilities may include the compound of Formula 1.

The compound in the EML may serve as a host. For example, the compound of Formula 1 may serve as a blue fluorescent host emitting blue light. The compound of Formula 1 in the emission layer may serve as a fluorescent or phosphorescent dopant emitting red light, green light, or blue light.

FIG. 1 is a schematic sectional view of an organic light-emitting device according to an embodiment. Hereinafter, a structure of an organic light-emitting device according to an embodiment and a method of manufacturing the same will now be described with reference to FIG. 1.

A substrate (not shown) may be any substrate that is used in existing organic light emitting devices. In some embodiments the substrate may be a glass substrate or a transparent plastic substrate with strong mechanical strength, thermal stability, transparency, surface smoothness, ease of handling, and water resistance.

The first electrode may be formed by depositing or sputtering a first electrode-forming material on the substrate. When the first electrode is an anode, a material having a high work function may be used as the first electrode-forming material to facilitate hole injection. The first electrode may be a reflective electrode or a transmission electrode. Transparent and conductive materials such as ITO, IZO, SnO₂, and ZnO may be used to form the first electrode. The first electrode may be formed as a reflective electrode using magnesium (Mg), aluminum (Al), aluminum-lithium (Al—Li), calcium (Ca), magnesium-indium (Mg—In), magnesium-silver (Mg—Ag), or the like.

The first electrode may have a single-layer structure or a multi-layer structure including at least two layers. For example, the first electrode may have a three-layered structure of ITO/Ag/ITO, but is not limited thereto.

An organic layer may be disposed on the first electrode.

The organic layer may include a hole injection layer (HIL), a hole transport layer (HTL), a buffer layer (not shown), an emission layer (EML), an electron transport layer (ETL), or an electron injection layer (EIL).

The HIL may be formed on the first electrode by vacuum deposition, spin coating, casting, Langmuir-Blodgett (LB) deposition, or the like.

When the HIL is formed using vacuum deposition, vacuum deposition conditions may vary according to the compound that is used to form the HIL, and the desired structure and thermal properties of the HIL to be formed. For example, vacuum deposition may be performed at a temperature of about 100° C. to about 500° C., a pressure of about 10⁻⁸ torr to about 10⁻³ torr, and a deposition rate of about 0.01 to about 100 Å/sec. However, the deposition conditions are not limited thereto.

When the HIL is formed using spin coating, the coating conditions may vary according to the material that is used to form the HIL, and the desired structure and thermal properties of the HIL to be formed. For example, the coating rate may be in the range of about 2,000 rpm to about 5,000 rpm, and a temperature at which heat treatment is performed to remove a solvent after coating may be in the range of about 80° C. to about 200° C. However, the coating conditions are not limited thereto.

The HIL may be formed of any material that is commonly used to form a HIL, in addition to the compound of Formula 1. Non-limiting examples of the material that can be used to form the HIL are N,N′-diphenyl-N,N′-bis-[4-(phenyl-m-tolyl-amino)-phenyl]-biphenyl-4,4′-diamine, (DNTPD), a phthalocyanine compound such as copper phthalocyanine, 4,4′,4″-tris(3-methylphenylphenylamino)triphenylamine (m-MTDATA), N,N′-di(1-naphthyl)-N,N′-diphenylbenzidine (NPB), TDATA, 2T-NATA, polyaniline/dodecylbenzenesulfonic acid (Pani/DBSA), poly(3,4-ethylenedioxythiophene)/poly(4-styrenesulfonate) (PEDOT/PSS), polyaniline/camphor sulfonic acid (Pani/CSA), and polyaniline)/poly(4-styrenesulfonate (PANI/PSS).

The thickness of the HIL may be from about 100 Å to about 10,000 Å, and in some embodiments, may be from about 100 Å to about 1,000 Å. When the thickness of the HIL is within these ranges, the HIL may have good hole injecting ability without a substantial increase in driving voltage.

Then, a HTL may be formed on the HIL by using vacuum deposition, spin coating, casting, Langmuir-Blodgett (LB) deposition, or the like. When the HTL is formed using vacuum deposition or spin coating, the conditions for deposition and coating may be similar to those for the formation of the HIL, though the conditions for the deposition and coating may vary according to the material that is used to form the HTL.

The HTL may be formed of the compound of Formula 1 or any known hole transporting materials. Non-limiting examples of suitable known HTL forming materials are carbazole derivatives, such as N-phenylcarbazole or polyvinylcarbazole, N,N′-bis(3-methylphenyl)-N,N′-diphenyl-[1,1-biphenyl]-4,4′-diamine (TPD), 4,4′,4″-tris(N-carbazolyl)triphenylamine (TCTA), and N,N′-di(1-naphthyl)-N,N′-diphenylbenzidine) (NPB).

The thickness of the HTL may be from about 50 Å to about 2,000 Å, and in some embodiments, from about 100 Å to about 1,500 Å. When the thickness of the HTL is within these ranges, the HTL may have good hole transporting ability without a substantial increase in driving voltage.

The H-functional layer (having both hole injection and hole transport capabilities) may contain at least one material from each group of the hole injection layer materials and hole transport layer materials. The thickness of the H-functional layer may be from about 500 Å to about 10,000 Å, and in some embodiments, may be from about 100 Å to about 1,000 Å. When the thickness of the H-functional layer is within these ranges, the H-functional layer may have good hole injection and transport capabilities without a substantial increase in driving voltage.

In some embodiments, at least one of the HIL, HTL, and H-functional layer may include at least one of a compound of Formula 300 below and a compound of Formula 350 below:

In Formulae 300 and 350, Ar₁₁, Ar₁₂, Ar₂₁, and Ar₂₂ may be each independently a substituted or unsubstituted C₅-C₆₀ arylene group.

In Formula 300, e and f may be each independently an integer from 0 to 5, for example, may be 0, 1, or 2. In a non-limiting embodiment, e may be 1, and f may be 0.

In Formulae 300 and 350 above, R₅₁ to R₅₈, R₆₁ to R₆₉, and R₇₁ to R₇₂ may be each independently a hydrogen atom, a deuterium atom, a halogen atom, a hydroxyl group, a cyano group, a nitro group, an amino group, an amidino group, a hydrazine group, a hydrazone, a carboxyl group or a salt thereof, a sulfonic acid group or a salt thereof, a phosphoric acid group or a salt thereof, a substituted or unsubstituted C1-C₆₀ alkyl group, a substituted or unsubstituted C₂-C₆₀ alkenyl group, a substituted or unsubstituted C₂-C₆₀ alkynyl group, a substituted or unsubstituted C₁-C₆₀ alkoxy group, a substituted or unsubstituted C₃-C₆₀ cycloalkyl group, a substituted or unsubstituted C₅-C₆₀ aryl group, a substituted or unsubstituted C₅-C₆₀ aryloxy group, or a substituted or unsubstituted C₅-C₆₀ arylthio group. In some embodiments, R₅₁ to R₅₈, R₆₁ to R₆₉, R₇₁, and R₇₂ may be each independently one of a hydrogen atom; a deuterium atom; a halogen atom; a hydroxyl group; a cyano group; a nitro group; an amino group; an amidino group; a hydrazine; a hydrazone; a carboxyl group or a salt thereof; a sulfonic acid group or a salt thereof; a phosphoric acid group or a salt thereof; a C₁-C₁₀ alkyl group (for example, a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, or the like); a C₁-C₁₀ alkoxy group (for example, a methoxy group, an ethoxy group, a propoxy group, a butoxy group, a pentoxy group, or the like); a C₁-C₁₀ alkyl group and a C₁-C₁₀ alkoxy group that are substituted with at least one of a deuterium atom, a halogen atom, a hydroxyl group, a cyano group, a nitro group, an amino group, an amidino group, a hydrazine, a hydrazone, a carboxyl group or a salt thereof, a sulfonic acid group or a salt thereof, and a phosphoric acid group or a salt thereof; a phenyl group; a naphthyl group; an anthryl group; a fluorenyl group; a pyrenyl group; and a phenyl group, a naphthyl group, an anthryl group, a fluorenyl group, and a pyrenyl group that are substituted with at least one of a deuterium atom, a halogen atom, a hydroxyl group, a cyano group, a nitro group, an amino group, an amidino group, a hydrazine, a hydrazone, a carboxyl group or a salt thereof, a sulfonic acid group or a salt thereof, a phosphoric acid group or a salt thereof, a C₁-C₁₀ alkyl group, and a C₁-C₁₀ alkoxy group.

In Formula 300, R₅₉ may be one of a phenyl group, a naphthyl group, an anthryl group, a biphenyl group, a pyridyl group; and a phenyl group, a naphthyl group, an anthryl group, a biphenyl group, and a pyridyl group that are substituted with at least one of a deuterium atom, a halogen atom, a hydroxyl group, a cyano group, a nitro group, an amino group, an amidino group, a hydrazine, a hydrazone, a carboxyl group or a salt thereof, a sulfonic acid group or a salt thereof, a phosphoric acid group or a salt thereof, a substituted or unsubstituted C₁-C₂₀ alkyl group, and a substituted or unsubstituted C₁-C₂₀ alkoxy group.

In an embodiment the compound of Formula 300 may be a compound represented by Formula 300A below:

In Formula 300A, R₅₁, R₆₀, R₆₁, and R₅₉ may be as defined above.

In some non-limiting embodiments, at least one of the HIL, HTL, and H-functional layer may include at least one of compounds represented by Formulae 301 to 320 below:

At least one of the HIL, HTL, and H-functional layer may further include a charge-generating material for improved layer conductivity, in addition to a known hole injecting material, hole transport material, and/or material having both hole injection and hole transport capabilities as described above.

The charge-generating material may be, for example, a p-dopant. The p-dopant may be one of quinine derivatives, metal oxides, and compounds with a cyano group, but are not limited thereto. Non-limiting examples of the p-dopant are quinone derivatives such as tetracyanoquinonedimethane (TCNQ), 2,3,5,6-tetrafluoro-tetracyano-1,4-benzoquinonedimethane (F4-CTNQ), and the like; metal oxides such as tungsten oxide, molybdenum oxide, and the like; and cyano-containing compounds such as Compound 200 below.

When the hole injection layer, hole transport layer, or H-functional layer further includes a charge-generating material, the charge-generating material may be homogeneously dispersed or inhomogeneously distributed in the layer.

A buffer layer may be disposed between at least one of the HIL, HTL, and H-functional layer, and the EML. The buffer layer may compensate for an optical resonance distance of light according to a wavelength of the light emitted from the EML, and thus may increase efficiency. The butter layer may include any hole injecting material or hole transporting material that are widely known. In some other embodiments, the buffer layer may include the same material as one of the materials included in the HIL, HTL, and H-functional layer that underlie the buffer layer.

Then, an EML may be formed on the HTL, H-functional layer, or buffer layer by vacuum deposition, spin coating, casting, LB deposition, or the like. When the EML is formed using vacuum deposition or spin coating, the deposition and coating conditions may be similar to those for the formation of the HIL, though the conditions for deposition and coating may vary according to the material that is used to form the EML.

The EML may include the compound of Formula 1. For example, the compound of Formula 1 may be used as a host or a dopant. The EML may be formed using a variety of known light-emitting materials, in addition to the compound of Formula 1. In some embodiments, the EML may also be formed using a known host and a dopant. Dopants that may be used to form the EML may include either a fluorescent dopant or a phosphorescent dopant which are widely known in the art.

Non-limiting examples of the host are Alq3, 4,4′-N,N′-dicarbazole-biphenyl (CBP), poly(n-vinylcarbazole) (PVK), 9,10-di(naphthalene-2-yl)anthracene (ADN), TCTA, 1,3,5-tris(N-phenylbenzimidazole-2-yl)benzene (TPBI), 3-tert-butyl-9,10-di-2-naphthylanthracene (TBADN), E3, distyrylarylene (DSA), dmCBP (see a formula below), and Compounds 501 to 509 below.

In some embodiments, an anthracene-based compound represented by Formula 400 below may be used as the host.

In Formula 400, Ar₁₁₁ and Ar₁₁₂ may be each independently a substituted or unsubstituted C₅-C₆₀ arylene group; Ar₁₁₃ to Ar₁₁₆ may be each independently a substituted or unsubstituted C₁-C₁₀ alkyl group, or a substituted or unsubstituted C₅-C₆₀ aryl group; and g, h, i, and j may be each independently an integer from 0 to 4.

In some non-limiting embodiments, Ar₁₁₁ and Ar₁₁₂ in Formula 400 may be each independently a phenylene group, a naphthylene group, a phenanthrenylene group, or a pyrenylene group; or a phenylene group, a naphthylene group, a phenanthrenylene group, a fluorenyl group, or a pyrenylene group that are substituted with at least one of a phenyl group, a naphthyl group, and an anthryl group.

In Formula 400 above, g, h, I, and j may be each independently 0, 1, or 2.

In Formula 400, Ar₁₁₃ to Ar₁₁₆ may be each independently one of a C₁-C₁₀ alkyl group that is substituted with at least one of a phenyl group, a naphthyl group, and an anthryl group; a phenyl group; a naphthyl group; an anthryl group; a pyrenyl group; a phenanthrenyl group; a fluorenyl group; a phenyl group, a naphthyl group, an anthryl group, a pyrenyl group, a phenanthrenyl group, and a fluorenyl group that are substituted with at least one of a deuterium atom, a halogen atom, a hydroxyl group, a cyano group, a nitro group, an amino group, an amidino group, a hydroxyrazine, a hydroxyrazone, a carboxyl group or a salt thereof, a sulfonic acid group or a salt thereof, a phosphoric acid group or a salt thereof, a C₁-C₆₀ alkyl group, a C₂-C₆₀ alkenyl group, a C₂-C₆₀ alkynyl group, a C₁-C₆₀ alkoxy group, a phenyl group, a naphthyl group, an anthryl group, a pyrenyl group, a phenanthrenyl group, and a fluorenyl group; and

but are not limited thereto.

For example, the anthracene-based compound of Formula 400 above may be one of the compounds represented by the following formulae, but is not limited thereto:

In some embodiments, an anthracene-based compound represented by Formula 401 below may be used as the host.

Ar₁₂₂ to Ar₁₂₅ in Formula 401 above may be defined as described above in conjunction with Ar₁₁₃ of Formula 400, and thus detailed descriptions thereof will not be provided here.

Ar₁₂₆ and Ar₁₂₇ in Formula 401 above may be each independently a C₁-C₁₀ alkyl group, for example, a methyl group, an ethyl group, or a propyl group.

In Formula 401, k and l may be each independently an integer from 0 to 4, for example, 0, 1, or 2.

For example, the anthracene-based compound of Formula 401 above may be one of the compounds represented by the following formulae, but is not limited thereto:

When the organic light-emitting device is a full color organic light-emitting device, the emission layer may be patterned into a red emission layer, a green emission layer, and a blue emission layer.

At least one of the red EML, the green EML, and the blue EML may include a dopant below (ppy=phenylpyridine).

Non-limiting examples of the blue dopant are compounds represented by the following formulae.

Non-limiting examples of the red dopant are compounds represented by the following formulae.

Non-limiting examples of the green dopant are compounds represented by the following formulae.

Non-limiting examples of the dopant that may be used in the EML are Pt complexes represented by the following formulae.

Non-limiting examples of the dopant that may be used in the EML are Os complexes represented by the following formulae.

When the EML includes both a host and a dopant, the amount of the dopant may be from about 0.01 to about 15 parts by weight based on 100 parts by weight of the host. However, the amount of the dopant is not limited to this range.

The thickness of the EML may be from about 100 Å to about 1,000 Å, and in some embodiments, from about 200 Å to about 600 Å. When the thickness of the EML is within these ranges, the EML may have good light emitting ability without a substantial increase in driving voltage.

Then, an ETL may be formed on the EML by vacuum deposition, spin coating, casting, or the like. When the ETL is formed using vacuum deposition or spin coating, the deposition and coating conditions may be similar to those for the formation of the HIL, though the deposition and coating conditions may vary according to a compound that is used to form the ETL. A material for forming the ETL may be the compound of Formula 1 above or any suitable material that can stably transport electrons injected from an electron injecting electrode (cathode). Non-limiting examples of materials for forming the ETL are a quinoline derivative, such as tris(8-quinolinorate)aluminum (Alq3), TAZ, BAlq, beryllium bis(benzoquinolin-10-olate (Bebq₂), 9,10-di(naphthalene-2-yl)anthracene (ADN), Compound 201, and Compound 202, but are not limited thereto.

The thickness of the HTL may be from about 100 Å to about 1,000 Å, and in some embodiments, from about 150 Å to about 500 Å. When the thickness of the ETL is within these ranges, the ETL may have satisfactory electron transporting ability without a substantial increase in driving voltage.

In some embodiments the ETL may further include a metal-containing material, in addition to any known electron-transporting organic compound.

The metal-containing material may include a lithium (Li) complex. Non-limiting examples of the Li complex are lithium quinolate (LiQ) and Compound 203 below:

Then, an EIL, which facilitates injection of electrons from the cathode, may be formed on the ETL. Any suitable electron-injecting material may be used to form the EIL.

Non-limiting examples of materials for forming the EIL are LiF, NaCl, CsF, Li₂O, and BaO, which are known in the art. The deposition and coating conditions for forming the EIL 18 may be similar to those for the formation of the HIL, though the deposition and coating conditions may vary according to the material that is used to form the EIL 18.

The thickness of the EIL may be from about 1 Å to about 100 Å, and in some embodiments, from about 3 Å to about 90 Å. When the thickness of the EIL is within these ranges, the EIL may have satisfactory electron injection ability without a substantial increase in driving voltage.

Finally, the second electrode is disposed on the organic layer. The second electrode may be a cathode that is an electron injection electrode. Material for forming the second electrode may be a metal, an alloy, an electro-conductive compound, which have a low work function, or a mixture thereof. In this regard, the second electrode may be formed of lithium (Li), magnesium (Mg), aluminum (Al), aluminum (Al), lithium (Li), calcium (Ca), magnesium (Mg)-indium (In), magnesium (Mg)-silver (Ag), or the like, and may be formed as a thin film type transmission electrode. In some embodiments, to manufacture a top-emission light-emitting device, the transmission electrode may be formed of indium tin oxide (ITO) or indium zinc oxide (IZO).

Although the organic light-emitting device of FIG. 1 is described above, other variations are possible.

When a phosphorescent dopant is used in the EML, a HBL may be formed between the HTL and the EML or between the H-functional layer and the EML by using vacuum deposition, spin coating, casting, Langmuir-Blodgett (LB) deposition, or the like, in order to prevent diffusion of triplet excitons or holes into the ETL. When the HBL is formed using vacuum deposition or spin coating, the conditions for deposition and coating may be similar to those for the formation of the HIL, although the conditions for deposition and coating may vary according to the material that is used to form the HBL. Any known hole-blocking material may be used. Non-limiting examples of hole-blocking materials are oxadiazole derivatives, triazole derivatives, and phenanthroline derivatives. For example, bathocuproine (BCP) represented by the following formula may be used as a material for forming the HBL.

The thickness of the HBL may be from about 20 Å to about 1,000 Å, and in some embodiments, from about 30 Å to about 300 Å. When the thickness of the HBL is within these ranges, the HBL may have improved hole blocking ability without a substantial increase in driving voltage.

According to embodiments, the organic light-emitting device may be included in various types of flat panel display devices, such as in a passive matrix organic light-emitting display device or in an active matrix organic light-emitting display device. In particular, when the organic light-emitting device is included in an active matrix organic light-emitting display device including a thin-film transistor, the first electrode on the substrate may function as a pixel electrode, electrically connected to a source electrode or a drain electrode of the thin-film transistor. Moreover, the organic light-emitting device may also be included in flat panel display devices having double-sided screens.

In some embodiments the organic layer of the organic light-emitting device may be formed of the compound of Formula 1 by using a deposition method or may be formed using a wet method of coating a solution of the compound of Formula 1.

Hereinafter, embodiments will be described in detail with reference to the following synthesis examples and other examples. However, these examples are for illustrative purposes only and are not intended to limit the scope thereof.

EXAMPLES Synthesis Example 1 Synthesis of Compound 2

Synthesis of Intermediate I-1

10.0 g (55.4 mmol) of 9,10-dihydrophenanthrene, 21.8 g (121.0 mmol) of N-bromosuccinimide, and 0.5 g (2.7 mmol) of p-TsOH were dissolved in 30 mL of acetonitrile, and then stirred at about 50° C. for about 12 hours. The reaction solution was cooled to room temperature, and stirred for about 30 minutes to precipitate crystals. The crystals were collected using a filter under reduced pressure, and then washed with methanol to obtain 8.4 g of Intermediate I-1 as gray crystals (Yield 45%). This compound was identified using liquid chromatography-mass spectroscopy (LC-MS). C₁₄H₁₀Br₂ M⁺ 335.9.

Synthesis of Intermediate I-2

5.0 g (15.0 mmol) of Intermediate I-1 was completely dissolved in 50 mL of dichloromethane, followed by an addition of 1.7 g (30.0 mmol) of nitric acid at room temperature to obtain a mixture. 1.5 g (15.0 mmol) of sulfuric acid was slowly dropwise added to the mixture and then stirred at about 30° C. for about 6 hours. After completion of the reaction, the reaction solution was cooled to room temperature. Then, 50 mL of methanol was added thereto and stirred for about 2 hours to precipitate crystals. The crystals were collected using a filter under reduced pressure, and then washed with methanol to obtain 5.2 g of Intermediate I-2 as yellow crystals (Yield 90%). This compound was identified using LC-MS. C₁₄H₉Br₂NO₂ M+ 380.9.

Synthesis of Intermediate I-3

4.6 g (12.0 mmol) of Intermediate I-2 was dissolved in 30 mL of o-dichlorobenzene, and heated until it was completely dissolved, followed by an addition of 4.7 g (18.0 mmol) of triphenylphosphine, and stirring at about 180° C. for about 3 hours. The reaction solution was cooled room temperature, and the solvent was evaporated from the solution. The residue was separated and purified using silica gel column chromatography, and washed with methanol to 2.9 g of Intermediate I-3 as white crystals (Yield 70%). This compound was identified using LC-MS. C₁₄H₁₁Br₂N M⁺ 350.9.

Synthesis of Intermediate I-4

10 g (10.0 mmol) of Intermediate I-3 was dissolved in 100 ml of toluene in an oxygen atmosphere, followed by an addition of 0.6 g (0.3 mmol) of 2,3-dichloro-5,6-dicyano-1,4-benzoquinone, and 0.2 g (0.3 mmol) of NaNO₂ thereto at room temperature to obtain a mixture, which was then stirred at about 110° C. for about 6 hours. After completion of the reaction, the reaction solution was cooled to room temperature. The solvent was evaporated from the solution. The residue was separated and purified using silica gel column chromatography to obtain 3.1 g of Intermediate I-4 (Yield 90%). This compound was identified using LC-MS. C₁₄H₇Br₂N M⁺ 346.8.

Synthesis of Intermediate I-5

3.4 g (10.0 mmol) of Intermediate I-4, 2.5 g (12.0 mmol) of iodobenzene, 0.2 g (1.0 mmol) of 1,10-phenanthroline, 0.2 g (2.0 mmol) of CuI, and 4.1 g (30.0 mmol) of K₂CO₃ were dissolved in 30 mL of N,N-dimethylformamide (DMF), and then stirred at about 80° C. for about 24 hours. The reaction solution was cooled to room temperature, and then extracted three times with 30 mL of water and 40 mL of diethylether. The organic phase was collected and was dried using magnesium sulfate to evaporate the solvent. The residue was separated and purified using silica gel column chromatography to obtain 3.8 g of Intermediate I-5 (Yield: 89%). This compound was identified using LC-MS. C₂₀H₁₁Br₂N M⁺ 422.9.

Synthesis of Compound 2

4.2 g (10.0 mmol) of Intermediate I-5, 4.8 g (22.0 mmol) of N-phenyl-1-naphthylamine, 0.37 g (0.4 mmol) of Pd₂(dba)₃, 0.08 g (0.4 mmol) of PtBu₃, and 2.9 g (30.0 mmol) of KOtBu were dissolved in 40 mL of toluene, and then stirred at about 85° C. for about 4 hours. The reaction solution was cooled to room temperature, and extracted three times with 30 mL of water and 30 mL of diethylether. The organic phase was collected and was dried using magnesium sulfate to evaporate the solvent. The residue was separated and purified using silica gel column chromatography to obtain 5.1 g of Compound 2 (Yield: 73%). This compound was identified using mass spectroscopy/fast atom bombardment (MS/FAB) and ¹H nuclear magnetic resonance (¹H NMR). C₅₂H₃₅N₃ cal. 701.28, found 702.31. ¹H NMR (CDCl₃, 400 MHz) δ 8.12-8.10 (m, 2H), 7.87-7.85 (m, 2H), 7.62-7.58 (m, 2H), 7.49-7.39 (m, 11H), 7.31 (d, 2H), 7.29 (s, 2H), 7.08-7.03 (m, 4H), 6.79 (d, 2H), 6.74-6.72 (dd, 2H), 6.65-6.51 (m, 2H), 6.11-6.08 (m, 4H).

Synthesis Example 2 Synthesis of Compound 50

Synthesis of Intermediate I-6

10.0 g (23.6 mmol) of Intermediate I-5 was dissolved in 100 mL of THF, and 10 mL (25.0 mmol) of n-BuLi (2.5M in hexane) was slowly dropwise added thereto at about −78° C. to obtain a mixture, which was then stirred for about 1 hour at the same temperature. Afterward, 9.3 mL (50.0 mmol) of 2-isoproxy-4,4,5,5,-tetramethyl-1,3,2-dioxaborolane was slowly dropwise added to the reaction solution, which was then stirred at about −78° C. for about 1 hour, and further at room temperature for 24 hours. After completion of the reaction, 50 mL of a 10% HCl aqueous solution, and 50 mL of H₂O were added thereto, and then extracted three times with 80 mL of diethylether. The organic phase was collected and was dried using magnesium sulfate to evaporate the solvent. The residue was separated and purified using silica gel column chromatography to obtain 8.1 g of Intermediate I-6 (Yield 73%). This compound was identified using LC-MS. C₂₆H₂₃BBrNO₂: M⁺ 471.1.

Synthesis of Intermediate I-8

4.7 g (10.0 mmol) of Intermediate I-6, 6.3 g (13.0 mmol) of Intermediate I-7, which was synthesized using a well-known method, 0.58 g (0.5 mmol) of Pd(PPh₃)₄, and 2.1 g (15.0 mmol) of K₂CO₃ were dissolved in 40 mL of a mixed solvent of THF/H₂O (2:1 by volume), and then stirred at about 80° C. for about 5 hours. After the reaction solution was cooled to room temperature, 40 mL of water was added to the reaction solution, which was then extracted three times with 50 mL of diethylether 50 mL. The organic phase was collected and was dried using magnesium sulfate to evaporate the solvent. The residue was separated and purified using silica gel column chromatography to obtain 5.4 g of Intermediate I-8 (Yield 72%). This compound was identified using LC-MS. C₅₁H₃₅BrN₂ M⁺ 754.2.

Synthesis of Compound 50

3.8 g (5.0 mmol) of Intermediate I-8, 1.0 g (6.0 mmol) of N,N-diphenylamine, 0.09 g (0.1 mmol) of Pd₂(dba)₃, 0.01 g (0.1 mmol) of PtBu3, 1.0 g (10.0 mmol) of KOtBu were dissolved in 20 mL of toluene, and then stirred at about 85° C. for about 4 hours. The reaction solution was cooled to room temperature, and then extracted three times with 20 mL or water and 20 mL of diethylether. The organic phase was collected and was dried using magnesium sulfate to evaporate the solvent. The residue was separated and purified using silica gel column chromatography to obtain 3.6 g of Compound 50 (Yield 85%). This compound was identified using mass spectroscopy/fast atom bombardment (MS/FAB) and ¹H NMR. C₆₃H₄₅N₃ cal. 843.36, found 844.42. ¹H NMR (CDCl₃, 400 MHz) δ 8.13-8.10 (m, 1H), 8.00 (d, 1H), 7.87-7.85 (m, 1H), 7.73 (d, 1H), 7.67-7.65 (ss, 1H), 7.62-7.58 (m, 3H), 7.53 (ss, 1H), 7.49-7.45 (m, 9H), 7.29-7.25 (s, 1H), 7.20 (d, 1H), 7.08-7.02 (m, 6H), 6.75-6.72 (m, 2H), 6.66-6.58 (m, 4H), 6.32-6.27 (m, 5H), 6.06-6.03 (m, 2H), 1.63 (s, 6H).

Synthesis Example 3 Synthesis of Compound 65

Synthesis of Intermediate I-9

4.7 g (10 mmol) of Intermediate I-6, 4.2 g (15.0 mmol) of 4-bromo-iodobenzene, 0.58 g (0.5 mmol) of Pd(PPh₃)₄, and 4.1 g (30.0 mmol) of K₂CO₃ were dissolved in 30 mL of a mixed solution of THF/H₂O (2:1 by volume), and then stirred at about 80° C. for about 5 hours. After the reaction solution was cooled to room temperature, 40 mL of water was added to the reaction solution, which was then extracted three times with 50 mL of ethylether. The organic phase was collected and was dried using magnesium sulfate to evaporate the solvent. The residue was separated and purified using silica gel column chromatography to obtain 3.1 g of Intermediate I-9 (Yield 62%). This compound was identified using LC-MS. C₂₆H₁₅Br₂N M⁺ 498.9.

Synthesis of Compound 65

2.5 g (5.0 mmol) of Intermediate I-9, 3.2 g (11.0 mmol) of 4-(diphenylamino) phenylboronic acid, 0.58 g (0.5 mmol) of Pd(PPh₃)₄, and 2.1 g (15.0 mmol) of K₂CO₃ were dissolved in a mixed solution of THF/H₂O (2:1 by volume), and then stirred at about 80° C. for about 5 hours. The reaction solution was cooled to room temperature, and then extracted three times with 30 mL of water and 30 mL of diethylether 30 mL. The organic phase was collected and was dried using magnesium sulfate to evaporate the solvent. The residue was separated and purified using silica gel column chromatography to obtain 2.7 g of Compound 65 (Yield: 67%). This compound was identified using MS/FAS and ¹H NMR. C₆₂H₄₃N₃ cal. 829.35, found 830.52. ¹H NMR (CDCl₃, 400 MHz) δ 8.06 (m, 1H), 8.01 (m, 1H), 7.85-7.82 (m, 2H), 7.73-7.70 (m, 2H), 7.62-7.58 (m, 2H), 7.56 (s, 2H), 7.53-7.51 (m, 2H), 7.46-7.44 (m, 3H), 7.40-7.36 (m, 1H), 7.30-7.26 (dd, 2H), 7.08-7.03 (m, 9H), 6.86-6.82 (m, 2H), 6.74-6.72 (m, 2H), 6.66-6.63 (m, 4H), 6.16-6.13 (m, 8H).

Additional compounds were synthesized using appropriate intermediate materials according to the synthetic pathways and the methods described as above, and were identified using ¹H NMR and MS/FAB. The results are shown in Table 1 below.

Synthetic pathways and source materials for other compounds not in Table 1 will be obvious to one of ordinary skill in the art based on the synthetic pathways and source materials described above.

TABLE 1 MS/FAB Compound ¹H NMR (CDCl₃, 400 MHz) δ found calc. 2 8.12-8.10 (m, 2H), 7.87-7.85 (m, 2H), 7.62-7.58 (m, 2H), 702.31 701.28 7.49-7.39 (m, 11H), 7.31 (d, 2H), 7.29 (s, 2H), 7.08-7.03 (m, 4H), 6.79 (d, 2H), 6.74-6.72 (dd, 2H), 6.65-6.51 (m, 2H), 6.11-6.08 (m, 4H) 3 7.64-7.58 (m, 6H), 7.53-7.45 (m, 10H), 7.42-7.38 (m, 5H), 754.35 753.31 7.32 (s, 2H), 7.10-7.05 (m, 4H), 6.78 (d, 2H), 6.69-6.62 (m, 6H), 6.38-6.34 (m, 4H), 1.87 (m, 6H), 1.84 (d, 6H) 4 7.78 (q, 1H), 7.75 (q, 1H), 7.64-7.58 (m, 8H), 7.53-7.46 (m, 967.55 969.50 .10H), 7.42 (t, 1H). 7.40-7.38 (m, 4H), 7.35-7.30 (m, 4H), 7.16 (d, 2H), 7.12-7.09 (m, 4H), 6.81-6.80 (d, 1H), 6.78 (d, 1H), 6.69-6.65 (m, 4H), 6.61 (m, 2H), 1.61 (s, 12H) 5 8.23-8.20 (m, 2H), 7.51-7.47 (m, 8H), 7.40 (s, 1H), 960.44 959.40 7.38-7.36 (m, 4H), 7.35 (d, 1H), 7.31-7.24 (m, 10H), 7.11-7.06 (m, 4H), 6.76 (d, 1H), 6.74 (d, 1H), 6.06-6.03 (m, 2H), 6.41-6.38 (m, 6H), 4.47-4.45 (m, 2H), 1.43-1.41 (m, 3H) 8 8.06-8.04 (m, 2H), 7.96-7.94 (m, 2H), 7.81-7.79 (m, 2H), 814.33 813.23 7.62-7.58 (m, 4H), 7.48-7.45 (m, 2H), 7.40-7.38 (m, 4H), 7.33 (s, 2H), 7.11-7.06 (m, 4H), 6.99-6.95 (m, 4H), 6.86 (d, 2H), 6.65-6.61 (m, 2H), 6.30-6.26 (m, 4H) 12 7.63-7.58 (m, 2H), 7.49-7.45 (m, 2H), 7.40-7.36 (m, 7H), 652.46 651.24 7.32 (s, 2H), 7.10-7.05 (m, 4H), 6.81-6.78 (m, 6H), 6.67-6.62 (m, 2H), 6.68-6.34 (m, 4H) 20 7.78 (t, 1H), 7.76 (t, 1H), 7.63-7.58 (m, 4H), 7.49-7.45 (m, 2H), 884.37 883.37 7.40-7.32 (m, 10H), 7.31 (s, 1H), 7.16 (d, 2H), 7.12-7.09 (m, 3H), 6.84-6.80 (m, 5H), 6.78 (d, 1H), 6.61 (dd, 2H), 1.61 (s, 12H). 23 7.63-7.58 (m, 2H), 7.49-7.45 (m, 2H), 7.40-7.36 (m, 7H), 746.54 745.33 7.32 (s, 2H), 7.10-7.05 (m, 4H), 6.78 (d, 2H), 6.75-6.71 (m, 4H), 6.67-6.62 (t, 1H), 6.65-6.62 (tt, 1H), 6.38-6.34 (m, 4H), 0.25-0.24 (s, 18H) 26 7.96-7.94 (m, 1H), 7.45 (d, 1H), 7.44 (d, 1H), 7.38 (d, 1H), 842.42 841.35 7.32 (s, 2H), 7.25-7.22 (m, 4H), 7.16 (d, 1H), 7.14-7.05 (m, 14H), 6.90-6.88 (dd, 1H), 6.84-6.81 (dd, 2H), 6.73 (d, 2H), 6.67-6.63 (m, 4H), 6.59 (d, 1H), 6.30-6.27 (m, 8H) 28 8.03-8.01 (m, 1H), 7.85-7.83 (m, 1H), 7.71-7.70 (d, 1H), 688.35 687.25 7.65-7.61 (m, 1H), 7.53-7.50 (m, 2H), 7.44-7.40 (m, 2H), 7.32 (s, 2H), 7.10-7.05 (m, 4H),), 6.99-6.93 (m, 4H), 6.78 (d, 2H), 6.67-6.62 (m, 2H), 6.56-6.50 (m, 5H), 6.38-6.34 (m, 4H) 32 8.37-8.31 (m, 1H), 7.96 (d, 1H), 7.54-7.47 (m, 4H), 795.40 794.34 7.40-7.27 (m, 9H), 7.16 (dd, 1H), 7.09-7.05 (m, 4H), 6.99-6.96 (m, 4H), 6.78 (d, 2H), 6.66-6.63 (m, 2H), 6.55-6.51 (m, 4H), 6.37-6.35 (m, 4H), 2.29 (s, 6H) 33 7.62-7.58 (m, 2H), 7.43-7.38 (m, 4H), 7.32 (s, 2H), 674.33 673.29 7.10-7.05 (m, 8H), 6.78 (d, 2H), 6.67-6.66 (t, 1H), 6.65 (t, 2H), 6.63-6.62 (t, 1H), 6.30-6.27 (m, 8H), 0.26 (s, 9H) 37 8.75-8.74 (m, 1H), 7.98 (t, 1H), 7.82-7.75 (m, 2H), 679.28. 678.28 7.59-7.57 (m, 1H), 7.46-7.44 (m, 1H), 7.39-7.38 (m, 2H), 7.32 (d, 2H), 7.27-7.26 (m, 2H), 7.09-7.05 (m, 8H), 6.80 (d, 2H), 6.66-6.63 (m, 4H), 6.29-6.27 (m, 8H) 40 8.90 (d, 1H), 8.60-8.58 (m, 1H), 8.12-8.10 (m, 1H), 729.43 728.29 7.93-7.91 (m, 1H), 7.85 (m, 1H), 7.62-7.58 (m, 2H), 7.46-7.35 (m, 8H), 7.33 (d, 3H), 7.27-7.24 (m, 3H), 7.09-7.03 (m, 4H), 6.87-6.84 (m, 2H), 6.78 (d, 2H), 6.74 (m, 1H), 6.66-6.61 (m, 2H), 6.37-6.35 (m, 2H), 6.10-6.08 (m, 2H) 43 8.23-8.20 (m, 1H), 7.62-7.54 (m, 2H), 7.51-7.45 (m, 6H), 767.35 766.31 7.40-7.35 (m, 5H), 7.32-7.24 (m, 6H), 7.11-7.05 (m, 6H), 6.79-6.78 (m, 2H), 6.76-6.74 (dd, 1H), 6.66-6.63 (m, 3H), 6.41-6.38 (m, 2H), 6.30-6.27 (m, 4H) 45 8.01 (m, 1H), 7.69-7.58 (m, 6H), 7.53-7.51 (m, 5H), 830.45 829.35 7.47-7.37 (m, 10H), 7.15 (d, 1H), 7.09-7.05 (m, 6H), 6.85 (d, 2H), 6.75-6.71 (m, 3H), 6.66-6.62 (m, 3H), 6.39-9.36 (m, 2H), 6.16-6.13 (m, 4H) 50 8.13-8.10 (m, 1H), 8.00 (d, 1H), 7.87-7.85 (m, 1H), 7.73 (d, 844.42 843.36 1H), 7.67-7.65 (ss, 1H), 7.62-7.58 (m, 3H), 7.53 (ss, 1H), 7.49-7.45 (m, 9H), 7.29-7.25 (s, 1H), 7.20 (d, 1H), 7.08-7.02 (m, 6H), 6.75-6.72 (m, 2H), 6.66-6.58 (m, 4H), 6.32-6.27 (m, 5H), 6.06-6.03 (m, 2H), 1.63 (s, 6H) 52 8.24-8.22 (m, 1H), 8.19-8.17 (m, 2H), 7.86-7.83 (dd, 1H), 868.45 867.36 7.78-7.76 (dd, 1H), 7.64-7.58 (m, 5H), 7.55 (s, 1H), 7.53-7.46 (m, 10H), 7.42-7.29 (m, 9H), 7.22-7.19 (m, 2H), 7.12-7.10 (m, 3H), 6.81-6.78 (dd, 1H), 6.6-6.78 (m, 2H), 6.61 (d, 1H), 1.61 (s, 6H) 53 8.12-8.10 (m, 2H), 8.03 (m, 1H), 7.64-7.60 (m, 6H), 828.44 827.33 7.55-7.49 (m, 7H), 7.47-7.33 (m, 17H), 7.30-7.25 (m, 3H), 6.77-6.73 (m, 5H) 57 8.17-8.15 (m, 2H), 8.01 (d, 2H), 7.87-7.85 (m, 2H), 854.43 853.35 7.62-6.58 (m, 2H), 7.56 (s, 2H), 7.51-7.36 (m, 13H), 7.26-7.25 (m, 2H), 7.23-7.21 (ss, 2H), 7.06-7.01 (m, 4H), 6.88-6.84 (m, 4H), 6.65-6.61 (m, 4H), 6.08-6.05 (m, 4H) 60 8.06 (d, 2H), 7.85-7.82 (m, 4H), 7.73-7.70 (m, 4H), 906.40 905.38 7.62-7.58 (m, 4H), 7.47-7.43 (m, 6H), 7.40-7.36 (m, 1H), 7.30 (d, 2H), 7.08-7.03 (m, 8H), 6.86-6.82 (m, 4H), 6.66-6.63 (m, 4H), 6.16-6.13 (m, 8H) 62 8.01-8.00 (m, 2H), 7.73 (d, 1H), 7.67-7.65 (ss, 1H), 870.45 869.38 7.62-7.58 (m, 5H), 7.53-7.51 (m, 3H), 7.46-7.44 (m, 2H), 7.40-7.38 (m, 1H), 7.28-7.26 (dd, 2H), 7.09-7.03 (m, 8H), 6.75-6.72 (m, 2H), 6.66-6.62 (m, 4H), 6.39 (d, 1H), 6.15-6.13 (m, 9H), 1.63 (s, 6H) 65 8.06 (m, 1H), 8.01 (m, 1H), 7.85-7.82 (m, 2H), 7.73-7.70 (m, 830.52 829.35 2H), 7.62-7.58 (m, 2H), 7.56 (s, 2H), 7.53-7.51 (m, 2H), 7.46-7.44 (m, 3H), 7.40-7.36 (m, 1H), 7.30-7.26 (dd, 2H), 7.08-7.03 (m, 9H), 6.86-6.82 (m, 2H), 6.74-6.72 (m, 2H), 6.66-6.63 (m, 4H), 6.16-6.13 (m, 8H)

Example 1

To manufacture an anode, a Corning 15 Ω/cm2 (1,200 Å) ITO glass substrate was cut to a size of 50 mm×50 mm×0.7 mm and then sonicated in isopropyl alcohol and pure water each for five minutes, and then cleaned by irradiation of ultraviolet rays for 30 minutes and exposure to ozone. The resulting glass substrate was loaded into a vacuum deposition device.

2-TNATA, was vacuum-deposited on the anode to a thickness of 600 Å to form an HIL, and Compound 2 as a hole transporting compound was vacuum-deposited on the HIL to a thickness of 300 Å to form a HTL.

9,10-Di-naphthalene-2-yl-anthracene (hereinafter, DNA) as a known blue fluorescent host, and 4,4′-bis[2-(4-(N,N-diphenylamino)phenyl)vinyl]biphenyl (hereinafter, DPAVBi) as a known blue fluorescent dopant, were co-deposited in a weight ratio of about 98:2 on the HTL to form an EML having a thickness of about 300 Å.

Then, Alg₃ was deposited on the EML to form an ETL having a thickness of 300 Å, and then LiF, which is a halogenated alkali metal, was deposited on the ETL to form an EIL having a thickness of 10 Å. Then, Al was vacuum-deposited on the EIL to form a cathode having a thickness of 3,000 Å, thereby forming an LiF/Al electrode and completing the manufacture of an organic light-emitting device.

The organic light-emitting device had a driving voltage of about 5.39V at a current density of 50 mA/cm², a luminosity of 2,540 cd/m², a luminescent efficiency of 5.57 cd/A, and a half life-span (hr @100 mA/cm²) of about 314 hours.

Example 2

An organic light-emitting device was manufactured in the same manner as in Example 1, except that Compound 4 was used, instead of Compound 2, to form the HTL.

The organic light-emitting device had a driving voltage of about 5.46V at a current density of 50 mA/cm², a luminosity of 2,225 cd/m², a luminescent efficiency of 5.61 cd/A, and a half life-span (hr @100 mA/cm²) of about 309 hours.

Example 3

An organic light-emitting device was manufactured in the same manner as in Example 1, except that Compound 5 was used, instead of Compound 2, to form the HTL.

The organic light-emitting device had a driving voltage of about 5.51V at a current density of 50 mA/cm², a luminosity of 2,764 cd/m², a luminescent efficiency of 5.56 cd/A, and a half life-span (hr @100 mA/cm²) of about 326 hours.

Example 4

An organic light-emitting device was manufactured in the same manner as in Example 1, except that Compound 12 was used, instead of Compound 2, to form the HTL.

The organic light-emitting device had a driving voltage of about 5.38V at a current density of 50 mA/cm², a luminosity of 2,961 cd/m², a luminescent efficiency of 5.24 cd/A, and a half life-span (hr @100 mA/cm²) of about 257 hours.

Example 5

An organic light-emitting device was manufactured in the same manner as in Example 1, except that Compound 23 was used, instead of Compound 2, to form the HTL.

The organic light-emitting device had a driving voltage of about 5.48V at a current density of 50 mA/cm², a luminosity of 2,780 cd/m², a luminescent efficiency of 5.48 cd/A, and a half life-span (hr @100 mA/cm²) of about 368 hours.

Example 6

An organic light-emitting device was manufactured in the same manner as in Example 1, except that Compound 37 was used, instead of Compound 2, to form the HTL.

The organic light-emitting device had a driving voltage of about 5.57V at a current density of 50 mA/cm², a luminosity of 2,695 cd/m², a luminescent efficiency of 5.31 cd/A, and a half life-span (hr @100 mA/cm²) of about 264 hours.

Example 7

An organic light-emitting device was manufactured in the same manner as in Example 1, except that Compound 40 was used, instead of Compound 2, to form the HTL.

The organic light-emitting device had a driving voltage of about 5.32V at a current density of 50 mA/cm², a luminosity of 2,813 cd/m², a luminescent efficiency of 5.62 cd/A, and a half life-span (hr @100 mA/cm²) of about 296 hours.

Example 8

An organic light-emitting device was manufactured in the same manner as in Example 1, except that Compound 50 was used, instead of Compound 2, to form the HTL.

The organic light-emitting device had a driving voltage of about 5.52V at a current density of 50 mA/cm², a luminosity of 2,961 cd/m², a luminescent efficiency of 5.59 cd/A, and a half life-span (hr @100 mA/cm²) of about 347 hours.

Example 9

An organic light-emitting device was manufactured in the same manner as in Example 1, except that Compound 52 was used, instead of Compound 2, to form the HTL.

The organic light-emitting device had a driving voltage of about 5.47V at a current density of 50 mA/cm², a luminosity of 2,780 cd/m², a luminescent efficiency of 5.58 cd/A, and a half life-span (hr @100 mA/cm²) of about 338 hours.

Example 10

An organic light-emitting device was manufactured in the same manner as in Example 1, except that Compound 57 was used, instead of Compound 2, to form the HTL.

The organic light-emitting device had a driving voltage of about 5.37V at a current density of 50 mA/cm², a luminosity of 2,695 cd/m², a luminescent efficiency of 5.63 cd/A, and a half life-span (hr @100 mA/cm²) of about 369 hours.

Example 11

An organic light-emitting device was manufactured in the same manner as in Example 1, except that Compound 65 was used, instead of Compound 2, to form the HTL.

The organic light-emitting device had a driving voltage of about 5.41V at a current density of 50 mA/cm², a luminosity of 2,813 cd/m², a luminescent efficiency of 5.60 cd/A, and a half life-span (hr @100 mA/cm²) of about 358 hours.

Comparative Example 1

An organic light-emitting device was manufactured in the same manner as in Example 1, except that 4,4′-bis[N-(1-naphthyl)-N-phenylamino]biphenyl (NPB) was used, instead of Compound 2, to form the HTL.

The organic light-emitting device had a driving voltage of about 7.35V at a current density of 50 mA/cm², a luminosity of 2,065 cd/m², a luminescent efficiency of 4.13 cd/A, and a half life-span (hr @100 mA/cm²) of about 145 hours.

The organic light-emitting devices manufactured using the compounds represented by Formula 1 according to embodiments as HTL materials had significantly lower driving voltages and improved I-V-L characteristics, as compared to those manufactured using a widely-known material NPB. In particular, the organic light-emitting devices according to the embodiments had markedly improved lifetimes. The characteristics of the organic light-emitting devices of Examples 1-11 and Comparative Example 1 are shown in Table 2 below.

TABLE 2 Driving Current Half-life span voltage density Luminance Efficiency Emission (hr HTL material (V) (mA/cm²) (cd/m²) (cd/A) color @100 mA/cm²) Example 1 Compound 2 5.39 50 2,540 5.57 Blue 314 hr Example 2 Compound 4 5.46 50 2,225 5.61 Blue 309 hr Example 3 Compound 5 5.51 50 2,764 5.56 Blue 326 hr Example 4 Compound 5.38 50 2,961 5.24 Blue 257 hr 12 Example 5 Compound 5.48 50 2,780 5.48 Blue 368 hr 23 Example 6 Compound 5.57 50 2,695 5.31 Blue 264 hr 37 Example 7 Compound 5.32 50 2,813 5.62 Blue 296 hr 40 Example 8 Compound 5.52 50 2,961 5.59 Blue 347 hr 50 Example 9 Compound 5.47 50 2,780 5.58 Blue 338 hr 52 Example 10 Compound 5.37 50 2,695 5.63 Blue 369 hr 57 Example 11 Compound 5.41 50 2,813 5.60 Blue 358 hr 65 Comparative NPB 7.35 50 2,065 4.13 Blue 145 hr Example 1

The novel condensed ring compound represented by Formula 1 above may have improved electrical characteristics and a charge transporting capability, and so, may be used as a hole injecting material or a hole transporting material that is suitable for any color fluorescent and phosphorescent devices, such as red, green, blue, and white fluorescent and phosphorescent devices. Therefore, organic light-emitting devices having high efficiency, low driving voltages, high luminance, and long lifetime may be manufactured using the compounds.

By way of summation and review, there is an ongoing desire for a material having improved electrical stability, high charge-transfer or emission capability, a high glass transition temperature, and capable of preventing crystallization, relative to existing unimolecular materials.

Embodiments provide a compound with improved characteristics, and a high-efficiency, low-voltage, high-luminance, and long-lifetime organic light-emitting device including the compound. The compound may have improved electrical characteristics, good charge transporting capabilities, improved emission capability, a high glass transition temperature (Tg) sufficient to prevent crystallization. The compound may be suitable as an electron transporting material for fluorescent or phosphorescent device of any color, or as a red green, blue, or white light-emitting material with higher emission efficiency and longer lifetime, and appropriate color coordinates, as compared with existing host materials.

While embodiments have been particularly shown and described with reference to exemplary embodiments thereof, it will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the spirit and scope thereof as defined by the following claims. 

What is claimed is:
 1. A compound represented by Formula 1 below:

wherein, in Formula 1, R₁ is a substituted or unsubstituted C1-C60 alkyl group, a substituted or unsubstituted C2-C60 alkenyl group, a substituted or unsubstituted C2-C60 alkynyl group, a substituted or unsubstituted C3-C60 cycloalkyl group, a substituted or unsubstituted C3-C60 cycloalkenyl group, a substituted or unsubstituted C5-C60 aryl group, a substituted or unsubstituted C2-C60 heteroaryl group, a substituted or unsubstituted C5-C60 aryloxy group, a substituted or unsubstituted C5-C60 arylthio group, or a substituted or unsubstituted C6-C60 condensed polycyclic group; Ar₁ to Ar₄ are each independently a substituted or unsubstituted C6-C60 aryl group, a substituted or unsubstituted C2-C60 heteroaryl group, or a substituted or unsubstituted C6-C60 condensed polycyclic group; and X and Y are each independently a single bond, a substituted or unsubstituted C6-C60 arylene group, a substituted or unsubstituted C2-C60 heteroarylene group, a substituted or unsubstituted C6-C60 condensed polycyclic group, or a divalent linking group formed by linking at least two of the substituted or unsubstituted C6-C60 arylene group, the substituted or unsubstituted C2-C60 heteroarylene group and the substituted or unsubstituted C6-C60 condensed polycyclic groups.
 2. The compound as claimed in claim 1, wherein, in Formula 1, at least two of Ar₁, Ar₂ and X are linked to one another to form a ring, or at least two of Ar₃, Ar₄ or Y are linked to each other to form a ring.
 3. The compound as claimed in claim 1, wherein, in Formula 1, R₁ is a group represented by one of Formulae 2a-2g:

wherein, in Formulae 2a to 2g, Q₀ and Q₁ are each independently a linking group represented by —C(R₃₀)(R₃₁)— or —N(R₃₂)—; Z₁, Z₂, R₃₀, R₃₁, and R₃₂ are each independently a hydrogen atom, a deuterium atom, a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, a substituted or unsubstituted C6-C20 condensed polycyclic group, —Si(R₄₀)₃, a halogen group, a cyano group, a nitro group, a hydroxy group or carboxy group; R₄₀ is a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, or a substituted or unsubstituted C6-C20 condensed polycyclic group; Y₁ to Y₃ are each independently C or N; p is an integer from 1 to 8; and * indicates a binding site to a nitrogen atom.
 4. The compound as claimed in claim 1, wherein, in Formula 1, Ar₁ to Ar₄ are each independently a group represented by one of Formulae 3a to 3d:

wherein, in Formulae 3a to 3d, Q₂ is a linking group represented by —C(R₃₀)(R₃₁)—, —N(R₃₂)—, —S—, or —O—; Z₁, R₃₀, R₃₁, and R₃₂ are each independently a hydrogen atom, a deuterium atom, a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, a substituted or unsubstituted C6-C20 condensed polycyclic group, —Si(R₄₀)₃, a halogen group, a cyano group, a nitro group, a hydroxy group, or a carboxy group; R₄₀ is a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, or a substituted or unsubstituted C6-C20 condensed polycyclic group; p is an integer from 1 to 7; and * indicates a binding site to a nitrogen atom.
 5. The compound as claimed in claim 1, wherein, in Formula 1, X and Y are each independently a group represented by one of Formulae 4a to 4g below:

wherein, in Formulae 4a to 4g, Q₃ is a linking group represented by —C(R₃₀)(R₃₁)—, —S—, or —O—; R₃₀ and R₃₁ are each independently a hydrogen atom, a deuterium atom, a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, a substituted or unsubstituted C6-C20 condensed polycyclic group, —Si(R₄₀)₃, a halogen group, a cyano group, a nitro group, a hydroxy group or carboxy group; R₄₀ is a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C5-C20 aryl group, a substituted or unsubstituted C3-C20 heteroaryl group, or a substituted or unsubstituted C6-C20 condensed polycyclic group; and * indicates a binding site to a carbon or nitrogen atom.
 6. The compound as claimed in claim 1, wherein the compound represented by Formula 1 is one of the following compounds:


7. An organic light-emitting device, comprising: a first electrode; a second electrode; and an organic layer between the first electrode and the second electrode, wherein the organic layer includes the compound of claim
 1. 8. The organic light-emitting device as claimed in claim 7, wherein: the organic light-emitting device includes a fluorescent or phosphorescent device, and the organic layer includes an emission layer in which the compound represented by Formula 1 is a host or dopant.
 9. The organic light-emitting device as claimed in claim 7, wherein the organic layer is a hole injection layer, a hole transport layer, or a functional layer having both hole injection and hole transport capabilities.
 10. The organic light-emitting device as claimed in claim 7, wherein: the organic light-emitting device includes an emission layer, an electron injection layer, an electron transport layer, a functional layer having both electron injection and transport capabilities; a hole injection layer, a hole transport layer, or a functional layer having both hole injection and transport capabilities, at least one of the hole injection layer, the hole transport layer, and the functional layer having both hole injection and hole transport capabilities further includes the compound represented by Formula 1, and the emission layer includes an anthracene-based compound, an arylamine-based compound, or a styryl-based compound.
 11. The organic light-emitting device as claimed in claim 7, wherein: the organic light-emitting device includes an emission layer, an electron injection layer, an electron transport layer, a functional layer having both electron injection and transport capabilities, a hole injection layer, a hole transport layer, or a functional layer having both hole injection and transport capabilities; at least one of the hole injection layer, the hole transport layer, and the functional layer having both hole injection and hole transport capabilities further includes the compound represented by Formula 1; and the emission layer includes red, green, blue, and white emission layers, one of which includes a phosphorescent compound.
 12. The organic light-emitting device as claimed in claim 11, wherein at least one of the hole injection layer, the hole transport layer, and the functional layer having both hole injection and hole transport capabilities further includes a charge-generating material.
 13. The organic light-emitting device as claimed in claim 12, wherein the charge-generating material is a p-dopant.
 14. The organic light-emitting device as claimed in claim 13, wherein the p-dopant is a quinine derivative, a metal oxide, or a cyano group-containing compound.
 15. The organic light-emitting device as claimed in claim 7, wherein the organic layer includes an electron transport layer, the electron transport layer including a metal complex.
 16. The organic light-emitting device as claimed in claim 15, wherein the metal complex is a Li complex.
 17. The organic light-emitting device as claimed in claim 15, wherein the metal complex is lithium quinolate (LiQ).
 18. The organic light-emitting device as claimed in claim 15, wherein the metal complex is Compound 203 below:


19. The organic light-emitting device of claim 7, wherein the organic layer is formed from the compound represented by Formula 1 using a wet process.
 20. A flat panel display device comprising the organic light-emitting device as claimed in claim 7, wherein the first electrode of the organic light-emitting device is electrically connected to a source electrode or a drain electrode of a thin-film transistor. 